Kan Inconel 600 worden gelast?
Inconel-chemische samenstelling
| Inconel | Ni | Cr | Fe | ma | Opmerking | Co | Mn | Cu | Al | Ti | Si | C | S | P | B |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 600 | 72 | 14.0-17.0 | 6.0-10.0 | 1 | 0.5 | 0.5 | 0.15 | 0.015 | |||||||
| 617 | 44.2-56.0 | 20.0-24.0 | 3 | 8.0-10.0 | 10.0-15.0 | 0.5 | 0.5 | 0.8-1.5 | 0.6 | 0.5 | 0.15 | 0.015 | 0.015 | 0.006 | |
| 625 | 58 | 20.0-23.0 | 5 | 8.0-10.0 | 3.15-4.15 | 1 | 0.5 | 0.4 | 0.4 | 0.5 | 0.1 | 0.015 | 0.015 | ||
| 690 | 59.5 | 30 | 9.2 | 0.35 | 0.01 | 0.02 | 0.35 | 0.019 | 0.003 | ||||||
| 718 | 50.0-55.0 | 17.0-21.0 | evenwicht | 2.8-3.3 | 4.75-5.5 | 1 | 0.35 | 0.2-0.8 | 0.65-1.15 | 0.3 | 0.35 | 0.08 | 0.015 | 0.015 | 0.006 |
| X-750 | 70 | 14.0-17.0 | 5.0-9.0 | 0.7-1.2 | 1 | 1 | 0.5 | 0.4-1.0 | 2.25-2.75 | 0.5 | 0.08 | 0.01 |
Laseigenschappen van Inconel 600
Bij Inconel 600-lassen is over het algemeen geen voorverwarming vereist. Wanneer de temperatuur van het basismetaal echter lager is dan 15 graden, moet het verbindingsgebied met een lengte van 250 mm tot 300 mm aan beide zijden worden voorverwarmd tot 15 graden tot 20 graden om poriën als gevolg van vochtcondensatie te voorkomen. Om korrelgroei en carbideprecipitatie te voorkomen, mag de interpasstemperatuur niet hoger zijn dan 100 graden. Er moet voor worden gezorgd dat snelle afkoeling, die tot porositeit kan leiden, wordt voorkomen. Het lasgebied moet vóór laswerkzaamheden zorgvuldig worden gereinigd.